JY·A132 for Titanium calcium type coating Cr19Ni10Nb which contains the Nb stabilizing property.

JY·A132 for Titanium calcium type coating Cr19Ni10Nb which contains the Nb stabilizing property. Featured Image
  • JY·A132 for Titanium calcium type coating Cr19Ni10Nb which contains the Nb stabilizing property.

JY·A132 for Titanium calcium type coating Cr19Ni10Nb which contains the Nb stabilizing property.

Is a kind of Titanium calcium type coating Cr19Ni10Nb which contains the Nb stabilizing property.It has good mechanical properties and    inter granular corrosion resistance. Good welding performance and porosity resistance. Heat resistance coating and crack resistance. AC/DC both can   be applied


Product Detail

Product Tags

Application

Purpose: Used for welding important corrosion resistant stainless steel this contains stable Ti such as 06Cr18Ni11Ti.

XXQ1
XXQ2
XXQ3

Chemical Composition of Welding Wires(%)

Test Item C Mn Si S P Cr Ni Mo Cu
Guarantee Value ≤0.08 0.50~2.50 ≤1.00 ≤0.030 ≤0.040 18.0～21.0 9.0～11.0 ≤0.75 ≤0.75
General Result 0.045 1.68 0.76 0.008 0.021 19.8 9.7 0.066 0.105

Mechanical Properties of Deposited Metal

Test Item Rm(MPa) A(%) Test Item Rm(MPa)
Guarantee Value ≥520 ≥25 Guarantee Value ≥520
General Result 630 41 General Result 630

Reference Current(DC+)

Diameter(mm) φ2.0 φ2.5 φ3.2 φ4.0
Amperage(A) 40~80 50~100 70~130 100~160

Note: 1.The electrode must be preheated at the temperature of 300°C for 1 hour.Preheat the rod whenever it is used
2.Preferred DC power supply,electric current should not be high.