JY·A102 Titanium calcium type coating Cr19Ni10 stainless steel electrode

JY·A102 is a kind of Titanium calcium type coating Cr19Ni10 stainless steel electrode.The deposited metal has good mechanical properties and inter granular corrosion resistance. It has good welding performance and porosity resistance. Heat resistance coating and crack resistance. AC/DC both can be applied.

Send email to us

Product Detail

Product Tags

Application

Purpose: Used for welding the corrosion resistant stainless steel structure, such as 06Cr19Ni10 and 06Cr18Ni¹1Ti and their working temperature should be below 300℃

Chemical Composition of Welding Wires(%)

Test Item	C	Mn	Si	S	P	Cr	Ni	Mo	Cu
Guarantee Value	≤0.08	0.50～2.50	≤1.00	≤0.030	≤0.040	18.0～21.0	9.0～11.0	≤0.75	≤0.75
General Result	0.041	1.35	0.69	0.008	0.022	19.5	9.6	0.064	0.1

Mechanical Properties of Deposited Metal

Test Item	Rm(MPa)	A(%)
Guarantee Value	≥550	30
General Result	600	42

Reference Current(DC+)

Diameter(mm)	φ2.0	φ2.5	φ3.2	Φ4.0	φ5.0
Amperage(A)	40~80	50~100	70~130	100~160	140~200

Note: 1.The electrode must be preheated at the temperature of 300°C for 1 hour.Preheat the rod whenever it is used
2.Preferred DC power supply,electric current should not be high.